PE-LLD REGRANULATE

PE-LLD regranulate - linear (stretch) white/green, 100% produced from waste silage stretch film. Used as a self-sucient raw material for the production of stretch films or as an additive for film and pipe reinforcement. The use of PE-LLD additive in film and pipe production improves the technical characteristics of the finished product, thus allowing for thickness reduction. Regranulate comes from our ongoing production – high and constant availability of 250-300 tons per month. Made from a single type of raw material (waste silage stretch film), high quality, stable, reproducible. High quality washing • Two-stage extrusion

WHITE

Tensile strengh at yield: >24Mpa @ 230C; 50 mm/min

Tensile strengh at break: 24 Mpa @ 230C; 50 mm/min

Melt Flow Index (MFI): 1,1-1,5 g/10min @ 2,16kg/190°C

Elongation at break 970%

Density: 0,922–0,932 g/cm3

Filtration: <100my

GREEN

Tensile strengh at yield: >24Mpa @ 230C; 50 mm/min

Tensile strengh at break: 24 Mpa @ 230C; 50 mm/min

Melt Flow Index (MFI): 1,0-1,5 g/10min @ 2,16kg/190°C

Elongation at break 930%

Density: 0,922–0,932 g/cm3

Filtration: <100my

PE-LD REGRANULATE

Used as self-sucient raw material for the production of films (bags, plastic dpc sheet). Regranulate comes from our ongoing production – availability of 20-40 tons per month. Made from a single type of raw material, high quality, stable, reproducible. High quality washing • Two-stage extrusion

Tensile strengh at yield: >21Mpa @ 230C; 50 mm/min

Tensile strengh at break: >21Mpa @ 230C; 50 mm/min

Melt Flow Index (MFI): 0,28-0,33 g/10min @ 2,16kg/190° C

Elongation at break 550%

Density: 0,940-0,942 g/cm³

Filtration: <100my

REGRANULATE 70% PE-LD / 30% PE-LLD

Regranulate 70% PE-LD / 30% PE-LLD – linear (stretch) - light grey. Regranulate is a blend of recyclates of PE-LD thick films and waste silage stretch film. Used as self-sucient raw material for the production of bags and plastic dpc sheet. Films made of this raw material are characterised by high performance, which makes it possible to reduce the thickness. Regranulate comes from our ongoing production – high and constant availability of 150-200 tons per month. Made from reproducible, high quality, stable raw materials. High quality washing • Two-stage extrusion

Tensile strengh at yield: >23Mpa @ 230C; 50 mm/min

Tensile strengh at break: >23Mpa @ 230C; 50 mm/min

Melt Flow Index (MFI): 0,8-0,9 g/10min @ 2,16kg/190°C

Elongation at break 730%

Density: 0,925-0,935 g/cm3

Filtration: <100my

CONTRACT PRODUCTION

Our equipment resources are high-quality grinding and washing plant and single screw and cascade extruders. We provide highest quality services of PE shredding, washing and regranulation. We provide contract production services of both post-consumer and post-production waste.